1、Hydroentangling is a mechanical bonding process involving the interlocking of fibers in a web structure using finc, closely spaced. high-pressure water jets. The main objective of this research was to investigate the rol

2、e of impact force and inclined water jets for improve on mechanical performance of hydroentangled fabrics. An experimental apparatus was designed with different inclination angles (-20°,-10°, 0°, +10°, +20°). The simulat

3、ion using Phoenics, version 3.4 CFD software was conducted to verify impact force experimental data of water jets flow. The predicted CFD impact force has good agreement with experimental data compared to calculated impa

4、ct force. The 60 gsm and 100 gsm fiber webs of bicomponent fibers (PET/COPET, PA6/COPET and PA6/PET) were manufactured and tested for their mechanical performance as well as evaluating fiber splitting within fiber webs.

5、The results show that with increases of water jets inclinationangle, impact force, and water jets pressure, the mechanical performance and fiber splittingof hydroentangled fabrics were enhanced. The water jets inclinatio

6、n angles of -10°& +10°shows higher mechanical performance followed by -20°& +20°and the last 0°, whilePA6/PET was highly split followed by PA6/COPET (split without dissolution of the sea)and PET/COPET did not split. It c

7、an be concluded that the combination of impact forceand inclined water jets with low inclination angles in appropriate conditions improved themechanical performance. The One Way of Analysis of Variance (ANOVA) and theMul